Nickel 200 Plate

Detect Metals' Workshop

Nickel 200 Sheet

ASTM N02200 Plate

EN 2.4066 Sheet

GB/T N6 pure nickel sheet

Characteristics

Nickel 200/201 is an unalloyed wrought nickel which have excellent resistance to many corrosive media from acid to alkaline.

excellent corrosion resistance in many alkaline media
good mechanical properties within a wide range of temperatures
magnetization decreasing continuously between -273 and 360 ℃and showing paramagnetism

Density: 8.89

Corrosion resistance

Nicel 200 and Nickel 201 have excellent resistance to many corrosive media from acid to alkaline. They are most useful under reducing conditions but, where a passive oxide is formed, they may also be used in oxidizing conditions. Their most significant property is extremely high resistance to caustic alkalies up to and including the molten state. The extra-low carbon content of Alloy 201 gives virtual mmunity to intergranular attack above about 315 ℃. The presence of chlorates must be kept to a minimum, as they accelerate the rate of attack. The resistance of Nickel 200 and Nickel 201 to mineral acids varies according to temperature and concentration and whether or not the solution is aerated. Corrosion resistance is better in deaerated acid. In acid, alkaline and neutral salt solutions, Nickel 200 and Nickel 201 show good resistance, but severe attack occurs in oxidizing salt solutions. Both alloys are resistant to all dry gases at room temperature. The low-carbon alloy can be used in dry chlorine and hydrogen chloride at temperatures up to 550 ℃.

Applications

Unalloyed wrought nickel combines excellent mechanical properties with good corrosion resistance. Above 300 ℃working temperature, the low-carbon version is generally used. The limited carbon content lowers mechanical property values and work-hardening rate but promotes ductility.

Typical applications are:

food production, such as handling of cooling brines, fatty acids and fruit juices resistance to acid, alkaline and neutral salt solutions and to organic acids.
vessels in which fluorine is generated and reacted with hydrocarbons resistance to fluorine
storing and transportation of phenol immunity from any form of attack ensures absolute product purity
manufacture and handling of sodium hydroxide, particularly at temperatures above 300 ℃.
Industrial processes where sodium hydroxide is typically used, involve:
production of hydrochloric acid and chlorination of hydrocarbons such as benzene, methane and ethane resistance at elevated temperatures to dry chlorine and hydrogen chloride
manufacture of vinyl chloride monomer resistance to hydrogen chloride at elevated temperatures

Chemical composition

	Ni	Fe	C	Mn	Si	Cu	Mg	Ti	S
200	>99.0	<0.40	<0.15	<0.35	<0.35	<0.25			<0.01
201	>99.0	<0.40	<0.02	<0.35	<0.35	<0.25			<0.01

Mechanical properties

	Condition	Yield Strength(Mpa)	Tensile Strength(Mpa)	Elongation(%)	Hardness(HB)
ASTM Min Value	Soft Annealed	105	380	40
Typical Values at RT	Hot Worked	196	431	50	90
Typical Values at RT	Cold Worked	490	588	25	160
Typical Values at RT	Soft Annealed	147	490	50	90

International Specification Comparison chart

	Material		Round Bar	Plate	Pipe
	Material		Round Bar	Plate	Seamless	Welded
ASTM	UNS N02200	UNS	B160	B162	B161/163	B725-730
ASME	UNS N02200	N02201	SB160	SB162	SB161-163
JIS	NW2200	NW2201	H4553	H4551	H4552
DIN	2.4066	2.4068	17752	17750	17751	17751

Product: Sheet, Coil, Pipe, Bar, Wire and Forgings

Product Name	Nickel 200 Plate
Brand	Tianjin Detai Co.,Ltd
Payment Acceptable	T/T,L/C
Port	Tianjin, Shanghai, Ningbo
Package	Wooden package , less than 2 tons per cases
Delivery time	within 15 working days

Nickel 200 Plate

Detect Metals' Workshop

Related Products